DIOFAN 193 D is a PVDC latex recommended for coating on plastic films intended to be used as a topcoat for rigid PVC films.

DIOFAN A 036 is a PVDC latex used as a flexible under layer for coating on polymer films, paper and cardboard, to be covered with an appropriate topcoat.

DIOFAN A 050 is a standard grade PVDC latex for coating on various substrates. It is generally used as a topcoat on paper and cardboard.

DIOFAN A 063 is a PVDC latex that exhibits good adhesion on corona treated polyolefin and PET films. This grade is specially recommended for the coating of extruded – laminated PE, and as an extrusion primer for PE on various substrates.

Diofan A 297 is an aqueous anionic dispersion, acidic and film-forming, of a copolymer with a high vinylidene chloride content.

DIOFAN A 586 is an anionic aqueous dispersion of vinylidene chloride/butyl acrylate/ methyl actylate terpolymer intended to be used as flame retardant binder for textiles and nonwovens.

DIOFAN A 716 is a low foaming high barrier PVDC latex. It is recommended for coating on PVC films.

DIOFAN A 736 is a PVDC latex intended to be used as a flexible underlayer for rigid PVC films, to be covered with an appropriate topcoat.

DIOFAN A 602 is an anionic aqueous dispersion of vinylidene chloride/butyl acrylate copolymer intended to be used in the building and textile industry.

DIOFAN A 610 is an anionic aqueous dispersion of vinylidene chloride/methyl acrylate copolymer intended to be used as high moisture barrier in the building industry.

DIOFAN B 201 is a high solid content PVDC latex with outstanding impermeability to gases and moisture. It is specifically recommended for the coating of plastic films.

Diofan^® P 510 is a newly developed polyvinylidene chloride copolymer, single component, water based dispersion.  Thanks to its unrivalled low moisture and water permeability, coatings based on Diofan^® P 510 exhibit outstanding corrosion resistance, even in the most severe environments. They provide excellent early water resistance, with overall performance equivalent to that obtained from traditional high performance solvent based paint systems (salt spray performance > 1000 h).

IXAN PNE 613 is a top coat for the coating of cellulosic or plastic films in a solvent mixture of tetrahydrofuran (THF) & toluene (TOL). This grade offers improved flexibility and sealing properties.

IXAN  PV 910 is a PVDC-preblend (2% ESO) for extrusion and coextrusion of films (heat shrinkable or not), and of thermoformable sheets. It is recommended for applications that require very good barrier.

IXAN PVS 815 is a PVDC-based premix for meat packaging and other applications. It can be extruded and coextruded to films (heat shrinkable or not), and to thermoformable sheets. It is recommended for applications that require very good barrier.

IXAN  SGA-1 is a copolymer based on vinylidene chloride and vinyl chloride monomers. The unrivalled performance of IXAN SGA-1 is due to the combination of its outstanding characteristics as adhesion combined with barrier as primer on a wide range of substrates, binding capabilities in e.g. print inks and paints, applicable as protective varnishes, solubility in a wide range of common organic solvents at room temperature, barrier properties and chemical resistance of the coatings and coverings, and heat-sealability, transparency, and glossiness of the coatings.